Sanmu 3355 resin is a soya fatty acid-modified alkyd resin.
| Parameter | Value |
|---|---|
| Appearance | Yellow transparent liquid |
| Solid content | 55±1% |
| Oil length | 34% |
| Acid value | ≤10 mg KOH/g |
| Hydroxyl value | 110 |
| Test Method | Store at 60°C for 7 days, measure viscosity change | |||||||
| Test Results | 6110A, 6915, and 6916 show good performance in both viscosity reduction and post-thickening control; 6110 shows significant viscosity increase after hot storage | |||||||
|
Performance Rating
|
6110 | 6110S | 6402 | 6110A | 6915 | 6916 | 6976A | 6500-50 |
| 4 | 6 | 6 | 8 | 8 | 8 | 6 | 6 | |
|
8 — Best, 6 — Good, 4 — Fair, 2 — Poor |
||||||||
| Test method | Store at 60°C for 7 days, measure gloss change | |||||||
| Test Result |
|
|||||||
|
Performance rating
|
6110 | 6110S | 6402 | 6110A | 6915 | 6916 | 6976A | 6500-50 |
| 4 | 8 | 6 | 4 | 4 | 8 | 8 | 6 | |
|
8 — Best, 6 — Good, 4 — Fair, 2 — Poor |
||||||||
| Test Method |
Test Method |
|||||||
| Test Results |
|
|||||||
|
Performance Rating
|
6110 | 6110S | 6402 | 6110A | 6915 | 6916 | 6976A | 6500-50 |
| 4 | 8 | 6 | 4 | 6 | 8 | 8 | 4 | |
|
8 — Best, 6 — Good, 4 — Fair, 2 — Poor |
||||||||
Core Advantage: Extreme viscosity reduction + high gloss.
Viscosity Performance:
Initial viscosity is only 925 mPa·s (one of the lowest in the entire system). After 7 days of hot storage, viscosity further decreases to 664 mPa·s — excellent stability.
Appearance Performance:
Achieves extremely high 60° gloss and L-value, with excellent distinctness of image (DOI) of the coating film.
Conclusion:
If you pursue high leveling during application and high fullness of the final coating film, 6916 is the best choice in the 3355 system.
Although the viscosity of 6976A is slightly worse than that of 6916, its gloss and L-value performance are still very good, making it a reliable backup option.